Evaluation of Mechanical Properties of Three dimensional Printed Flexible Denture Resin according to Post-polymerization Conditions: A Pilot Study

Abstract

Purpose: The purpose of this study was to evaluate whether three-dimensional (3D)-printed flexible denture resin has suitable mechanical properties for use as a thermoplastic denture base resin material. Materials and Methods: A total of 96 specimens were prepared using the 3D printed flexible denture resin (Flexible Denture). Specimens were designed in CAD software (Tinkercad) and printed through a digital light-processing 3D printer (Asiga MAX UV). Post-polymerization process was conducted according to air exposure or glycerin im mersion at 35°C or 60°C and for 30 or 60 minutes. The maximum flexural strength, elastic modulus, 0.2% offset yield strength, and Vickers hardness of 3D-printed flexible denture resin were assessed. Result: The maximum flexural strength ranged from 64.46±2.03 to 84.25±4.32 MPa, the 0.2% offset yield strength ranged from 35.28±1.05 to 46.13±2.33 MPa, the elastic modulus ranged from 1,764.70±64.66 to 2,179.16±140.01 MPa, and the Vickers hardness ranged from 7.01±0.40 to 11.45±0.69 kg/mm2 . Conclusion: Within the limits of the present study, the maximum flexural strength, 0.2% offset yield strength, elastic modulus, and Vickers hardness are sufficient for clinical use under the post-polymerization conditions of 60°C at 60 minutes with or without glycerin precipitation.