Effects of artificial aging on the biaxial flexural strength of Ce-TZP/Al2O3 and Y-TZP after various occlusal adjustments

Authors
 Il-Gwang Sim  ;  Yooseok Shin  ;  June-Sung Shim  ;  Jong-Eun Kim  ;  Jee-Hwan Kim 
Citation
 CERAMICS INTERNATIONAL, Vol.43(13) : 9951-9959, 2017 
Journal Title
 CERAMICS INTERNATIONAL 
ISSN
 0272-8842 
Issue Date
2017
Keywords
Zirconia ; Occlusal adjustment ; Low-temperature degradation ; Flexural strength
Abstract
The aim of this study was to determine the effect of aging on the biaxial flexural strength (BFS) of Ce-TZP/Al2O3 and Y-TZP after occlusal adjustment. NanoZr block (Ce-TZP/Al2O3 nanocomposite) and Katana zirconia block (Y-TZP) were prepared by milling with the aid of CAD/CAM into disk-shaped specimens. For each type of zirconia, 16 specimens were prepared without grinding for the control group (diameter of 16 mm and thickness of 1.20±0.05 mm, mean±SD), while 48 specimens were prepared for 3 experimental groups (n=16 each; 16 mm in diameter and 1.50±0.05 mm thick) with different types of surface grinding: superfine diamond bur (group I), zirconia stone bur (group II), and zirconia stone and fine polishing bur (group III). These specimens underwent an aging process in a steam autoclave for 5 h at 0.2 MPa and 134 °C, and then X-ray diffractometry was applied along with measurements of surface roughness and BFS. After occlusal adjustment, the monoclinic phase percentage increased in 3 experimental groups. Overall the increase was greater for Ce-TZP/Al2O3 than for Y-TZP. The Ra value showed similar changes for both types of zirconia. Following the aging process, Y-TZP showed a greater increase in the monoclinic phase percentage, but the change was not statistically significant. The Ra value showed similar changes in both types of zirconia, with no significant differences between before and after the aging process. The results of the BFS test showed that applying the aging process after grinding significantly increased the strength of both types of zirconia, with Ce-TZP/Al2O3 being significantly stronger than Y-TZP. The specimens treated by a superfine diamond bur exhibited the highest BFS in the four tested groups. Ce-TZP/Al2O3 had a higher BFS and greater resistance to low-temperature degradation than did Y-TZP.
Full Text
https://www.sciencedirect.com/science/article/pii/S0272884217308076
DOI
10.1016/j.ceramint.2017.05.005
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Prosthodontics (보철과학교실) > 1. Journal Papers
2. College of Dentistry (치과대학) > Dept. of Conservative Dentistry (보존과학교실) > 1. Journal Papers
Yonsei Authors
Kim, Jong Eun(김종은) ORCID logo https://orcid.org/0000-0002-7834-2524
Kim, Jee Hwan(김지환) ORCID logo https://orcid.org/0000-0002-0872-4906
Shin, Yoo Seok(신유석) ORCID logo https://orcid.org/0000-0003-1121-2570
Shim, June Sung(심준성) ORCID logo https://orcid.org/0000-0003-1428-0122
URI
https://ir.ymlib.yonsei.ac.kr/handle/22282913/160250
사서에게 알리기
  feedback

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse

Links