Preliminary Investigation of Bone Cement Using Calcium Phosphate Glass

Authors
 Byung Hyun Lee  ;  Min Chul Kim  ;  Yong Keun Lee  ;  Racquel Z. LeGeros  ;  Chong Kwan Kim  ;  Seong Ho Choi  ;  Kwang Mahn Kim  ;  Kyoung Nam Kim 
Citation
 Key Engineering Materials, Vol.284~286 : 109-112, 2005 
Journal Title
Key Engineering Materials
ISSN
 1013-9826 
Issue Date
2005
MeSH
Bone Cement ; Calcium Phosphate Glass Cement ; Compressive Strength ; Setting Time
Keywords
Bone Cement ; Calcium Phosphate Glass Cement ; Compressive Strength ; Setting Time
Abstract
The mixed pastes of binary calcium phosphate glass with Ca/P ratio of 0.6 and distilled water were set after about 4 hr, while never set when calcium phosphate glass with Ca/P lower than 0.5. Their compressive strength was ranged from 16.0 to 23.3 MPa. When Na2HPO4 solution was used instead of distilled water as liquid phase, the setting time became drastically much shorter. As the mole concentration of Na2HPO4 solution increased from 0.25 M to 2 M, setting time was shortened to 35 min from almost 3 hr, but compressive strength decreased from 28.8 MPa to 13.2 MPa. At constant mole concentration, as the mass ratio of a powder to liquid ratio increased, setting time was shortened and maximum compressive strength was measured when a powder/liquid ratio was 2.5. However, no crystallized phases were detected either during setting or after complete setting. The XRD , FT-IR and SEM examinations indicated that calcium phosphate glass dissolved and then glass phase precipitated again. We concluded, therefore, that Na2HPO4 just affected the kinetics of dissolution and precipitation of CPG. The mechanism of hardening has yet to be studied.
Full Text
http://www.scientific.net/KEM.284-286.109
DOI
10.4028/www.scientific.net/KEM.284-286.109
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Dental Biomaterials and Bioengineering (치과생체재료공학교실) > 1. Journal Papers
2. College of Dentistry (치과대학) > Dept. of Periodontics (치주과학교실) > 1. Journal Papers
Yonsei Authors
Kim, Kyoung Nam(김경남)
Kim, Kwang Mahn(김광만) ORCID logo https://orcid.org/0000-0002-5235-0294
Kim, Min Chul(김민철)
Kim, Chong Kwan(김종관)
Lee, Yong Keun(이용근)
Choi, Seong Ho(최성호) ORCID logo https://orcid.org/0000-0001-6704-6124
URI
https://ir.ymlib.yonsei.ac.kr/handle/22282913/114809
사서에게 알리기
  feedback

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse

Links