즉시 상아질 봉쇄와 지연 상아질 봉쇄에 따른 상아질 접착의 미세인장 결합강도 비교

Other Titles
 The comparison of microtensile bond strength with immediate and delayed dentin sealing 
 이흥배  ;  한종현  ;  심준성  ;  김선재 
 Journal of Korean Academy of Prosthodontics (대한치과보철학회지), Vol.46(4) : 372-380, 2008 
Journal Title
Journal of Korean Academy of Prosthodontics(대한치과보철학회지)
Issue Date
Immediate dentin sealing ; Delayed dentin sealing ; Dentin bonding ; Microtensile bond strength
Purpose: The purpose of this study was to evaluate the effect of various methods of dentin bonding agent application on microtensile bond strength between dentin and resin, using a 2-step etch-and-rinse dentin bonding agent. Material and methods: Twenty freshly extracted human molars were obtained and divided into 4 groups of 5 teeth. 2-step etch-and-rinse dentin bonding agent was used for all groups. The control specimens were prepared using a direct immediate bonding technique. The delayed dentin sealing (A, C) specimens were prepared using an indirect approach with delayed dentin sealing. For group A, resin was built-up on uncured dentin bonding agent, and for group C, resin was built-up on pre-cured dentin bonding agent. Preparation of the immediate dentin sealing (B) specimens also used an indirect approach with immediate dentin sealing immediately following preparation. All teeth were prepared for a microtensile bond strength test. Specimens were stored in water for 24 hours. Ten beams (1.0 x 1.0 x 11 mm) from each tooth were selected for testing. Bond strength data (MPa) were analyzed with a one-way ANOVA test, and post hoc comparison was done using the Scheffe's test. Results: The mean microtensile bond strengths of control group, B and C (DDS with pre-cure) were not statisticaaly different from each other at 32.7, 33.3, 34.2 MPa. the bond strength for group A (DDS without pre-cure), 19.5 MPa, was statistically different (P < .01) from the other 3 groups. Conclusion: When preparing teeth for indirect bonded restorations, DDS with pre-curing dentin bonding agent and IDS results in the same bond strength between dentin and resin. On the contrast, the bond strength was decreased when DDS without pre-curing dentin bonding agent was used.
Files in This Item:
T200800669.pdf Download
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Prosthodontics (보철과학교실) > 1. Journal Papers
Yonsei Authors
Kim, Sun Jai(김선재) ORCID logo https://orcid.org/0000-0002-0828-8008
Shim, June Sung(심준성) ORCID logo https://orcid.org/0000-0003-1428-0122
Han, Jong Hyoun(한종현)
사서에게 알리기


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.