Effects of ultraviolet and simvastatin treatment on titanium implants placed in rabbit tibia

Abstract

Effects of ultraviolet (UV) treatment and simvastatin (SIM) immersion on the osseointegration of sandblasted, large-grit, acid-etched (SLA) titanium dental implants were evaluated at two different time points in rabbit tibias, with or without xenogeneic bone graft material. Implants were categorized into four groups according to the surface treatment type. Twelve rabbits received two implants per tibia. A tibial defect model was created using a trephine bur, with implants in contact with the bone surface and bovine bone graft materials for gap filling. The rabbits were sacrificed after 2 or 4 weeks. UV treatment or SIM immersion increased bone-to-implant contact (BIC) on native sides and BIC and bone area (BA) on grafted sides. The application of both treatments did not result in higher BIC or BA than a single treatment. It could be concluded that UV or SIM treatment of SLA titanium implants promotes osseointegration and new bone formation in tibias with or without xenogeneic bone graft material.

본 연구에서는 토끼의 경골에 큰 입자를 표면에 분사하고 산부식한 표면을 가진 SLA (sandblasted, large-grit, acid-etched) 티타늄 치과 임플란트에 자외선 조사 및 심바스타틴 침지를 하였을 때 골유착에 어떠한 영향을 미치는지 두 가지 시점(時点)에서 평가하였다. 임플란트는 표면처리 방법에 따라 네 가지 군으로 분류되었다. 열 두 마리의 토끼에 대하여 한 경골 당 두 개의 임플란트를 식립하였다. 트레핀 버를 이용해 경골에 원형 결손부를 형성하였고, 임플란트가 골 표면에 접촉할 수 있도록 결손부의 한 쪽에 기대어 식립하였으며 간격에는 소 뼈 이식재를 채워 넣었다. 토끼는 2주 또는 4주 후 희생되었다. 자외선 조사 또는 심바스타틴 침지는 골 이식을 하지 않은 부위에서 골-임플란트 접촉(bone-to-implant contact, BIC)을 유의하게 증가시켰고, 골 이식을 한 부위에서는 BIC와 골 면적(bone area, BA)를 모두 유의하게 증가시켰다. 두 방법을 모두 적용하는 것은 단일 방법을 적용하는 것과 비교하였을 때 더 나은 결과를 보이지 않았다. 이상의 결과에 따라, SLA 티타늄 임플란트에 자외선 조사 또는 심바스타틴 침지를 하는 것은 토끼의 경골에서 골유착과 신생골 형성을 촉진한다고 결론지을 수 있다.