Push-Out Bond Strength Evaluation of Fiber-Reinforced Composite Resin Post Cemented with Self-Adhesive Resin Cement Using Different Adhesive Bonding Systems

Abstract

The purpose of this in vitro study was to evaluate the push-out bond strength of fiber-reinforced resin posts using self-adhesive cements with different adhesive systems. A total of 50 single-rooted human maxillary premolars with fully developed apices and 15-16 mm straight root canals were selected. The teeth were divided into 10 groups with coronal and apical parts according to the adhesive bonding system and luting material used: one universal adhesive with MDP-containing self-adhesive resin cement; another universal adhesive with MDP-containing self-adhesive resin cement; universal primer with MDP-containing self-adhesive resin cement; universal primer with dual-cure resin cement; MDP-containing self-adhesive resin cement only (Control). Each specimen was subjected to a fatigue load of 600,000 cycles using a chewing simulator with sliding movement and cut horizontally for push-out bond strength testing. Statistical evaluation consisted of a one-way ANOVA test using SPSS v23.0. The highest bond strength (7.05 MPa) was obtained in the coronal part of the Single Bond universal group treated with MDP-containing self-adhesive resin cement and the lowest strength (4.77 MPa) was observed in apical part of MDP-containing self-adhesive resin cement group (Control). However, the one-way ANOVA results showed no significant difference between all 10 groups (p > 0.05). The self-adhesive cement without adhesive bonding showed no statistically different value compared to self-adhesive cements with adhesive bonding.