Glass fiber post와 composite resin core의 전단결합강도

Other Titles
 A study for the bonding strength of composite resin core to glass fiber post 
Authors
 김태형  ;  심준성  ;  이근우 
Citation
 Journal of Korean Academy of Prosthodontics (대한치과보철학회지), Vol.43(4) : 415-425, 2005 
Journal Title
 Journal of Korean Academy of Prosthodontics (대한치과보철학회지) 
ISSN
 0301-2875 
Issue Date
2005
MeSH
Glass fiber post ; Surface treatment ; Bond strength
Keywords
Glass fiber post ; Surface treatment ; Bond strength
Abstract
Statement of problem: Fracture of composite resin core will be occurred by progress of crack. Bonding interface of different materials has large possibility of starting point of crack line. Therefore, the bond strength of glass fiber post to composite resin core is important for prevention of fracture. Purpose: This in vitrostudy tried to find out how to get the higher strength of glass fiber post to composite resin core through surveying the maximum load that fractures the post and core complex. Materials & Methods: 40 specimens made with glass fiber Posts(Style post(R), Metalor, Swiss) and composite resin core(Z-100(R), 3M, USA) were prepared and loaded to failure with push-outtype shear-bond strength test in a universal test machine. The maximum fracture load and fracture mode were investigated in the specimens that were restored with four different surface treatments. With the data, ANOVA test was used to validate the significance between the test groups, and Bonferroni method was used to check if there is any significant statistical difference between each test group. Every analysis was approved with 95% reliance. Results: On measuring the maximum fracture load of specimens, both the treatments of sandblasted and acid-etched one statistically showed the strength increase rather than the control group(p<0.005). The scanning electric microscope revealed that sand blasting made more micro-retention form not only on the resin matrix but on the glass fiber, and acid-etching contributed to increase in surface retention form, eliminated the inorganic particles in resin matrix. Specimen fracture modes investigation represented that sand blasted groups showed lower bonding failure than no-sand blasted groups. Conclusion: Referring to the values of maximum fracture load of specimens, the bonding strength was increased by sand blasting and acid-etching.
Files in This Item:
T200500543.pdf Download
DOI
OAK-2005-03717
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Prosthodontics (보철과학교실) > 1. Journal Papers
Yonsei Authors
Shim, June Sung(심준성) ORCID logo https://orcid.org/0000-0003-1428-0122
Lee, Keun Woo(이근우) ORCID logo https://orcid.org/0000-0002-3153-190X
URI
https://ir.ymlib.yonsei.ac.kr/handle/22282913/150928
사서에게 알리기
  feedback

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse