차아염소산나트륨 용액과 고압증기멸균이 근관치료용 니켈-타이타늄 파일의 주기적 피로 파절에 미치는 영향

Other Titles
 Cyclic fatigue of the sodium hypochlorite treated and /or steam autoclaved nickel-titanium endodontic files 
Authors
 조혜영  ;  정일영  ;  이찬영  ;  김의성 
Citation
 Journal of Korean Academy of Operative Dentistry (대한치과보존학회지), Vol.33(1) : 54-65, 2008 
Journal Title
 Journal of Korean Academy of Operative Dentistry (대한치과보존학회지) 
ISSN
 1225-0864 
Issue Date
2008
Keywords
Ni-Tiendodontic files ; cyclic fatigue fracture ; sodium hypochloritesolution ; steam autoclave
Abstract
The purpose of this study was to determine the effect of sodium hypochlorite and steam autoclaving on the cyclic fatigue of nickel-titanium endodontic files. Two types of files with a .06 taper and #30 were used, $K3^®$ (SybronEndo, Glendora, California, USA) and Hero $642^®$(Micro-Mega, BesanCon, France). The files were divided into 6 experimental groups containing 10 files each group depending the soaking time in 6% sodium hypochlorite solution and number of cycles of steam autoclave. After sterilization, a cyclic fatigue test was performed on each file, and the fracture time was recorded in seconds. The control group underwent the cyclic fatigue test only. After the test, the surface characteristics of the files were observed using scanning electron microscopy (SEM). All groups containing the Hero 64~ files showed a similar cyclic fatigue fracture time. However, the cyclic fatigue fracture time with the $K3^®$ files was significantly shorter in groups which were treated with sodium hypochlorite than in the control group (P < 0.05), SEM revealed both Hero $642^®$ and $K3^®$ files to have significant corrosion on the file surface in groups treated with sodium hypochlorite, compared with the sharp and regular blades of the control group. $K3^®$ files showed more corrosion than the Hero $642^®$ files. Bluntness of the blades of the $K3^®$ file was observed in groups treated with steam autoclave. Although there was no obvious destruction on the surface of steam autoclaved Hero $642^®$ files, slight bluntness was observed. Sterilizing with a steam autoclave is much less destructive to $K3^®$ files than sodium hypochlorite. The longer time exposed to sodium hypochlorite, the more destructive pattern was shown on the blades of the files. Therefore, when using sodium hypochlorite solution, the exposure time should be as short as possible in order to prevent corrosion and increase the cyclic fatigue fracture time.
Files in This Item:
T200800827.pdf Download
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Conservative Dentistry (보존과학교실) > 1. Journal Papers
Yonsei Authors
Kim, Eui Seong(김의성) ORCID logo https://orcid.org/0000-0003-2126-4761
Lee, Chan Young(이찬영)
Jung, Il Young(정일영) ORCID logo https://orcid.org/0000-0001-8972-2664
URI
https://ir.ymlib.yonsei.ac.kr/handle/22282913/107100
사서에게 알리기
  feedback

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse