알루미나 테이프를 사용한 유리 침투형 알루미나 코아의 변연적합도

Other Titles
 MARGINAL FIT OF GLASS INFILTRATED ALUMINA CORE FABRICATED FROM ALUMINA TAPES 
Authors
 오남식  ;  이명현  ;  김대준  ;  이근우  ;  이선형 
Citation
 Journal of Korean Academy of Prosthodontics (대한치과보철학회지), Vol.36(6) : 832-845, 1998 
Journal Title
 Journal of Korean Academy of Prosthodontics (대한치과보철학회지) 
ISSN
 0301-2875 
Issue Date
1998
Abstract
The purpose of this study was to compare the marginal fit of all ceramic crowns prepared from alumina slip casting, which is consistent with the conventional In-ceram system, and those fabricated from alumina tapes which is currently under development in an effort to alleviate complexities involved in the forming procedure of the In-ceram crown core. All ceramic crowns, made of In-ceram(slip casting) and alumina tapes(Doctor blade casting), were prepared with 90degreeand 135degreeshoulder margins. The crowns were cemented with a glass ionomer cement and embeded in epoxy resin. The embedded crowns were sectioned faciolingually and mesiodistally and marginal discrepancies and marginal gaps were measured under the Measurescope MM II. The measurements were analyzed using Wilcoxon rank sum test and Kruskal-Wallis test and the results were as follows: 1. In the case of 90degreeshoulder margin, the combined marginal discrepancies and marginal gaps were 78.3 micrometerm and 44.4 micrometer respectively, for the all ceramic crowns fabricated using the alumina tapes. In comparison, the values were 65 micrometer and 25.5 micrometer for the In-ceram crowns. For the marginal gaps a statistical difference existed (p<0.05) but no significant difference was observed for the marginal discrepancy (p>0.05). 2. In the case of 135degreeshoulder margin, the combined marginal discrepancy and marginal gaps were 82.1 micrometer and 40.2 micrometer respectively, for the all ceramic crowns formed with the tapes. As compared with the marginal discrepancy and gaps of the 90degreeshoulder margin in the fabricated from the alumina tapes, no significant statistical differencies were discerned in both cases (p>0.05). 3. There was no statistically significant difference in the fits among four locations around the margins of the all ceramic crowns fabricated using the alumina tapes. The results obtained in this study showed that the marginal fits of the glass infiltrated alumina cores fabricated from the alumina tapes are slightly higher value than those prepared using the In-ceram but the difference is within a clinically acceptable range.
Files in This Item:
T199802592.pdf Download
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Prosthodontics (보철과학교실) > 1. Journal Papers
Yonsei Authors
Lee, Keun Woo(이근우) ORCID logo https://orcid.org/0000-0002-3153-190X
URI
https://ir.ymlib.yonsei.ac.kr/handle/22282913/176878
사서에게 알리기
  feedback

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse

Links