치과 재료용 NiTi 합금의 특성에 대한 Ag 첨가의 영향

Other Titles
 Effect of silver addition on the properties of NiTi alloy for dental application 
 오근택  ;  박기호  ;  심형민  ;  황충주  ;  김경남 
 Journal of the Korean Research Society for Dental Materials (대한치과기재학회지), Vol.28(4) : 289-296, 2001 
Journal Title
 Journal of the Korean Research Society for Dental Materials (대한치과기재학회지) 
Issue Date
Shape memory alloy ; Superelasticity ; NiTi alloy ; Silver ; TTR ; Corrosion resistance
Equiatomic and near-equiatomic nickel-titanium alloys have shape memory effect and superelasticity. However nickel-titanium alloys are extremely sensitive to the precise nickel-titanium ratio and alloying additions. There are many reports on the alloying additions such as Fe, Al, Cr, Co, V, Pt, Zr, Hf, Nb and Cu. The purpose of this study was to investigate the effect of silver addition to nickel-titanium alloy for dental and medical application. Arc melting process was used to fabricate nickel-titanium alloys. The casts were heat-treated in a vacuum furnace at 950℃ for 72 hours to homogenize their composition. Subsequently, they were hot-rolled at 950℃ to obtain the plate samples and annealed in a vacuum furnace at 950℃. To investigate the properties of nickel-titanium alloys, phases, transformation temperature, compositions, corrosion resistance and hardness were evaluated using X-ray diffractometer, differential scanning calorimeter, energy dispersive spetroscopy or atomic absorption spectroscopy, potentiostat and micro-vickers hardness tester, respectively. NiTiAg alloys showed the low silver recovery rate for the cast due to its low evaporation temperature, and showed low silver solubility to NiTi alloy. Silver addition to NiTi alloy increased transition temperature range (TTR) above 100℃ and stabilized martensitic phase(monoclinic structure) at room temperature because Ms temperature was above room temperature. Martensitic and austenitic phase existed in x-ray diffraction pattern of solution annealed NiTiAg alloys. The silver addition is considered to improve corrosion resistance and change largely the mechanical properties depending upon the amount of alloying addition and types of addition elements.
Full Text
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Dental Biomaterials and Bioengineering (치과생체재료공학교실) > 1. Journal Papers
Yonsei Authors
Kim, Kyoung Nam(김경남)
사서에게 알리기


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.