Effect of Low-Concentration Hydrofluoric Acid Etching on Shear Bond Strength and Biaxial Flexural Strength After Thermocycling

Authors
 You-Jung Kang  ;  Yooseok Shin  ;  Jee-Hwan Kim 
Citation
 MATERIALS, Vol.13(6) : e1409, 2020-03 
Journal Title
 MATERIALS 
Issue Date
2020-03
Keywords
flexural strength ; hot etching ; hydrofluoric acid ; shear bond strength ; zirconia
Abstract
This study evaluated the shear bond strength (SBS) and biaxial flexural strength (BFS) of resin cements according to the surface treatment method using low-temperature hot etching with hydrofluoric acid (HF) on a yttrium-stabilized tetragonal zirconia (Y-TZP) surface; 96 discs and 72 cubes for BFS and SBS tests for Y-TZP were randomly divided into four groups of BFS and three groups of SBS. Specimens were subjected to the following surface treatments: (1) no treatment (C), (2) air abrasion with 50 μm Al2O3 particles (A), (3) hot etching with HF at 100 °C for 10 min (E), and (4) air abrasion + hot etching (AE). After treatments, the specimens were coated with primer, and resin cement was applied with molds. The specimens were evaluated for roughness (Ra) via scanning electron microscopy and x-ray diffraction, and the data were analyzed by an analysis of variance (ANOVA) and Kruskal-Wallis tests. Group E produced significantly higher SBS compared to group A and AE before and after thermocycling. The BFSs of all groups showed no significant differences before thermocycling; however, after thermocycling, C and E treatment groups were significantly higher compared to group A and AE. All groups showed phase transformation. Group E was observed lower monoclinic phase transformation compared to other groups.
Files in This Item:
T202001290.pdf Download
DOI
10.3390/ma13061409
Appears in Collections:
2. College of Dentistry (치과대학) > Dept. of Prosthodontics (보철과학교실) > 1. Journal Papers
2. College of Dentistry (치과대학) > Dept. of Conservative Dentistry (보존과학교실) > 1. Journal Papers
Yonsei Authors
Kim, Jee Hwan(김지환) ORCID logo https://orcid.org/0000-0002-0872-4906
Shin, Yoo Seok(신유석) ORCID logo https://orcid.org/0000-0003-1121-2570
URI
https://ir.ymlib.yonsei.ac.kr/handle/22282913/176075
사서에게 알리기
  feedback

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse

Links